Nzube nke annealing bụ ime ka onye nduzi n'ihi na ebu tensile usoro n'ihi lattice mgbanwe na hardening nke waya site a ụfọdụ okpomọkụ okpomọkụ, nke mere na molekụla lattice rearrangement mgbe mgbake nke usoro chọrọ nke nro, n'otu oge ahụ na-ewepụ onye nduzi n'elu ihe fọdụrụ lubricants, mmanụ, wdg, n'oge tensile usoro dị mfe aha, na elled waya.
Ihe kachasị mkpa bụ ijide n'aka na waya enamelled nwere nro kwesịrị ekwesị na elongation n'oge a na-eji ikuku eme ihe, mgbe ọ na-enyere aka melite conductivity.
Nke buru ibu nke nrụrụ ogo nke onye nduzi, na-ebelata elongation na ike dị elu.
Ngwunye waya ọla kọpa, nke a na-ejikarị eme ihe n'ụzọ atọ: nkwụsị diski; Annealing na-aga n'ihu na igwe ịse waya; Na-aga n'ihu na-annealing na igwe lacquer. Ụzọ abụọ mbụ enweghị ike izute ihe achọrọ nke teknụzụ mkpuchi. Ngwunye diski nwere ike ime ka waya ọla kọpa dị nro, ma mmanụ ahụ ezughị ezu, n'ihi na waya ahụ dị nro mgbe ọ kwụsịrị, na-ehulata na-abawanye mgbe eriri ahụ kwụsịrị.
Na-aga n'ihu na-eme ka ọ dị nro na igwe ịse waya nwere ike ime ka waya ọla kọpa dị nro ma wepụ griiz dị n'elu, ma mgbe ọ gbasasịrị, eriri ọla kọpa dị nro na-emerụ ahụ na eriri waya iji mee ka ọ na-ehulata ọtụtụ. Na-aga n'ihu annealing tupu eserese na agba igwe nwere ike ọ bụghị nanị nweta nzube nke nro na-ewepụ mmanụ, ma na annealed waya bụ ogologo, ozugbo n'ime agba ngwaọrụ, nwere ike ntekwasa na edo agba film.
Ekwesịrị ikpebi okpomọkụ nke ọkụ ọkụ na-ekpo ọkụ dị ka ogologo nke ọkụ ọkụ, nkọwa waya ọla kọpa na ọsọ ahịrị. N'otu ọnọdụ okpomọkụ na ọsọ, ka ọkụ na-ekpo ọkụ na-adịte aka, otú ahụ ka ọ na-eweghachite lattice nduzi nke ọma. Mgbe annealing okpomọkụ dị ala, na elu ọkụ okpomọkụ, mma elongation, ma ndị na-abụghị onu pụtara mgbe annealing okpomọkụ dị nnọọ elu, na elu okpomọkụ, ndị nta na elongation, na elu nke waya ida luster, na ọbụna mfe imebi.
Igwe ọkụ na-ekpo ọkụ na-ekpo ọkụ dị oke elu, ọ bụghị nanị na-emetụta ndụ ọrụ nke ọkụ ahụ, kamakwa ọ dị mfe ịkụnye ahịrị ahụ mgbe ọ kwụsịrị na imecha. A na-achọ ka a na-achịkwa okpomọkụ kachasị nke ọkụ ọkụ na ihe dịka 500 ℃. Ọ dị irè ịhọrọ isi njikwa okpomọkụ n'ọnọdụ ndị yiri ya nke ọnọdụ okpomọkụ na-agbanwe agbanwe.
Ọla kọpa dị mfe oxidize na elu okpomọkụ, ọla kọpa oxide bụ nnọọ rụrụ, agba film enweghị ike ike ike na-ejikọta ya na ọla kọpa waya, ọla kọpa oxide nwere catalytic mmetụta na ịka nká nke agba film, na mgbanwe nke enameled waya, thermal ujo, thermal ịka nká nwere mmetụta ọjọọ. Iji ọla kọpa waya adịghị oxidized, ọ dị mkpa iji mee ka ọla kọpa waya na elu okpomọkụ na-enweghị kọntaktị na oxygen na ikuku, n'ihi ya, e kwesịrị inwe ihe nchebe gas. Ọtụtụ ọkụ ọkụ na-ekpo ọkụ na-ekpuchi mmiri n'otu akụkụ ma meghee n'akụkụ nke ọzọ.
Mmiri dị na sink na-ekpo ọkụ ọkụ nwere ọrụ atọ: ọ na-emechi ọkụ ahụ, na-eme ka waya dị jụụ, na-emepụta uzuoku dị ka gas nchebe. Ná mmalite nke ụgbọala n'ihi na annealing tube nke obere uzuoku, enweghị ike ịbụ n'oge nke ikuku, annealing tube nwere ike jupụta na obere ego nke mmanya ngwọta (1: 1). (Kpachara anya ka ị ghara ị drinkụ mmanya dị ọcha ma chịkwaa ego ejiri mee ya)
Ogo mmiri dị na tank nke annealing dị ezigbo mkpa. Ihe na-adịghị mma na mmiri ga-eme ka waya adịghị ọcha ma na-emetụta agba, na-enweghị ike ịmepụta ihe nkiri na-egbuke egbuke. Ọdịnaya chlorine nke mmiri a na-eji kwesịrị ịbụ ihe na-erughị 5mg/l na ngbanwe eletrik kwesịrị ịbụ ihe na-erughị 50μΩ/cm. Mgbe oge ụfọdụ gasịrị, ions chloride na-ejikọta n'elu waya ọla kọpa ga-emebi waya ọla kọpa na ihe nkiri agba, na-ebute ntụpọ ojii n'elu waya ahụ na ihe nkiri agba nke enamelled waya. A ga-ehichapụkwa olulu mmiri mgbe niile iji hụ na ọ dị mma.
A na-achọkwa okpomọkụ mmiri dị na sink. Mmiri dị elu dị elu na-eme ka ikuku mmiri dị na mmiri iji chebe waya ọla kọpa annealing, waya na-ahapụ tank adịghị mfe iji weta mmiri, ma na-ajụ oyi nke waya. Ọ bụ ezie na mmiri dị ala na-arụ ọrụ dị jụụ, enwere mmiri dị ukwuu na waya, nke na-adịghị mma maka eserese. Ọtụtụ mgbe, ahịrị gbara ọkpụrụkpụ na-adị jụụ ma eriri dị mkpa na-ekpo ọkụ. Mgbe waya ọla kọpa na-ahapụ n'elu mmiri ma mee ka ọ na-egbuke egbuke, mmiri ọkụ dị oke elu.
N'ozuzu, oké akara na-achịkwa na 50 ~ 60 ℃, n'etiti akara na-achịkwa na 60 ~ 70 ℃, na ezi akara na-achịkwa na 70 ~ 80 ℃. N'ihi nnukwu ọsọ na nsogbu mmiri siri ike, waya dị mkpa kwesịrị ịkpọ nkụ site na ikuku ọkụ.